What Is The Difference With Crazing to Crack In An Opal?

処理...

Many opal cutters will sell stones that have cracks or crazing in their opals. There is a major difference between the two and we will show you what it is. While there is nothing wrong with buying an Opal that is crazed or cracked it is important that the buyer is made aware before the purchase. If your Opal does have fracture lines in it or it has crazed do not put it in an ultrasonic cleaner as it may destroy the Opal.

CRACKS

A crack can be a minor or major fault line. It can be on the surface or internal. If you see a line inside the opal and it reflects light then it is a crack in the stone. External cracks will decrease the value / price more than internal cracks.

Internal cracks have been shown to be stable and not continue to grow. Some Opal miners have stones with cracks inside them that have had no movement. External crack lines in a polished opal can be cut out but obviously this decreases the size and value of the Opal.

Cracked opals do not necessarily mean that they will fall apart. Many cracked opals will hold but the biggest problem is if an opal is cracked and in a ring, the everyday wear and tear and knocks will break the Opal. Many cracked opals are set as pendants for this reason and are able to be worn most of the time.

CRAZING

Crazing looks like multiple crack lines. Crazed opal is mostly kept as specimens or collectors pieces. They are not recommended for use in Jewelry. Crazed opals can be treated with Opticon which stabilises the Opal.

The image above is an Ethopian Opal with an inclusion. Notice there is no light reflection.

Inclusions are not cracks. Many opals contain natural inclusions. These can be air bubbles, vegetation matter and even potch.

AUSTRALIAN OPAL

Most Australian opal is very stable with black opal [N1] considered the most stable due to its smaller molecules. Generally Australian Opal that displays a crack is set at 10-20% of the value of a stable opal of similar qualities. It is estimated only around 1-3% of Australian opals crack but some opal fields are more susceptible than others.

Most Australian Opals contain 3-5% water. Generally the deeper the miner digs the more water content the Opal will have. Mines at Lighting Ridge go down to about 30 meters and the miner can gauge how stable the Opal is. As the potch goes from tough dry material to soggy wet potch then it is an indication of stable material. When they go deeper and the miner knows that this opal will obviously have more water content.

Most Australian opals are non porous and therefore they do not absorb water.

POTCH LINES

Some opals may show veins or spider web lines. These are not cracks but potch lines. It is easy for the cutter to check as crack lines reflect light but potch lines do not. Potch lines do decrease the value of the opal depending on the severity of lines. They do not generally effect the stability of the opal.

ETHIOPIAN OPAL

Ethiopian opal is a Hydrophane opal. Hydrophane opal absorbs water. When Ethiopian opal is dehydrated the base is more opaque. when the opal is hydrated it becomes more transparent. Transition time from hydrated to dehydrated can vary from minutes to days but most Opals do transition in a few hours.

FRACTURE TESTING ETHIOPIAN OPAL

Gemstones have been fractured or cleavage tested for centuries to test parting or cleavage in rough material. All major carving or cutting centres fracture test material before cutting or carving.

Even before modern testing techniques were invented rough material was still tested. During winter a wood fire would warm up a room and cold water was splashed repeatedly on the rough.

Today this basic process is still used for opals by soaking the opals in water and drying them in a warm but not hot environment. This processes can be repeated several times before the cutting process starts. Some opal with a small crack line will sometimes expand under water.

This process tests the stress points and cracks will appear on the weakest cleavage point. The opal is now ready for cutting and polishing to remove any visible cracks.

Fractures or crazing and cracks can appear as:

granular sugary patterns
smooth even breaks
rough edged irregular breaks

Cutters obviously make decision to cut an opal after it has been fractured tested as to observe which side of the opal the fracture occurs on. This involves great skill and a professional cutter will cut according to the directions that have opened up when the fracture is complete.

It takes a cutter many years of experience to understand the best approach to cutting an opal. Master opal cutters will charge a percentage cutting fee for top stones from 3 to 5% and in most cases this is worth paying!

OPTICON STABILIZATION

Opticon is the most common form for stabilising opal. Immerse the stones in a canning style jar filled with enough Opticon to cover the stones and tighten the lid so water can not escape. Condensation can turn the resin cloudy.

Place the jar in a ordinary slow cooker filled with enough water so the jar dose not float.
Turn the heat up to 150-170 degrees Celsius (302 - 338 Fahrenheit)
use a thermometer to check the temperature. We recommend using a kitchen meat thermometer.
Cook for 24 hours
Strain off the excess resin and place on tinfoil

Use a vacuum machine like the ones used to vacuum food bags. This sucks the air out of the bag.

Vacuum for at least one hour.
Using an artist style brush paint the stone with a weak mixture [40 to 1] of resin and hardener and re vacuum for 15 minutes.
Remove any excess moisture with a acetone cloth.
When the stones are no longer tacky polish or re-polish

This 54.7 carat Harlequin pattern opal was sold for over $1,100. When it was cut 5 years ago it displayed crazed lines. The owner treated the stone with Opticon and sold it for around 10% of its value if it was untreated.

GLUES

You can also coat the stone with super glue and heat it under strong lights. The glass like covering over the stone gives it stability while it is polished.

BOULDER OPAL

Boulder opal is mostly formed on an ironstone backing and is stable. This ironstone can be A deep brown chocolate color to sandy ironstone with a light brown colour. Ironstone does help to keep the opal stable. Some crack lines may appear at a 45% degree angel but the opal can still be stable. Some boulder crystal opal may also display cracks. Koroit and Yowah opal fields are considered stable.

MEXICAN OPAL

Most Mexican opal is stable. Crazed or cracked opals can occur when the potch and opal cut in one piece as each has different pressure threshold.

U.S.A. OPALS

USA Opals are generally not considered to be stable and opals are mostly made in to Triplets or stabilised. USA opals tend to craze as water content can go up to 14%

BRAZILIAN OPALS

These are generally considered stable as the water content is mostly less than 5%. The opals are semi translucent to white translucent.

HONDURAN OPAL

Honduras opal on matrix is considered stable but some crystal formed on matrix may display crack lines

Browse Our Opals

Black Opal

Boulder Opal

Crystal Opal

Ethiopian Opal

多くのオパールカッターは、オパールにひび割れやひび割れがある石を販売します。 2つの間に大きな違いがあり、それが何であるかをお見せします。ひびが入っているまたはひびが入っているオパールを購入することには何の問題もありませんが、購入前に購入者に知らせておくことが重要です。オパールに割れ目が入っている場合やひびが入っている場合は、超音波洗浄機に入れないでください。オパールが破壊される可能性があります。

ひび

亀裂は、マイナーまたはメジャーの断層線です。表面または内部に配置できます。オパールの内側に線があり、それが光を反射している場合、それは石の亀裂です。外部亀裂は、内部亀裂よりも価値/価格を下げます。

内部亀裂は安定しており、成長し続けないことが示されています。一部のオパール鉱山労働者は、動きのない内部に亀裂のある石を持っています。磨かれたオパールの外部亀裂線を切り取ることができますが、明らかにこれによりオパールのサイズと価値が減少します。

ひび割れたオパールは、必ずしもバラバラになるとは限りません。多くのひびの入ったオパールが保持されますが、最大の問題は、オパールにひびが入ってリング状になっている場合、日常の磨耗やノックによりオパールが壊れることです。多くのひびの入ったオパールがこの理由でペンダントとして設定されており、ほとんどの時間着用することができます。

クレイジー

ひび割れは複数の亀裂線のように見えます。クレイズドオパールは、ほとんどが標本またはコレクターピースとして保管されます。ジュエリーでの使用は推奨されません。クレイジーオパールは、オパールを安定させるオプティコンで処理できます。

上の画像は、含まれているエトピアのオパールです。光の反射がないことに注意してください。

含有物は亀裂ではありません。多くのオパールには天然の封入物が含まれています。これらは、気泡、植生物質、さらには鉢植えです。

オーストラリアのオパール

ほとんどのオーストラリア産オパールは非常に安定しており、ブラックオパール[N1]はその分子が小さいため、最も安定していると考えられています。一般に、亀裂を示すオーストラリアのオパールは、同様の品質の安定したオパールの値の10〜20％に設定されています。オーストラリアのオパールの1〜3％にしか亀裂がないと推定されていますが、一部のオパールフィールドは他のフィールドよりも影響を受けやすくなっています。

ほとんどのオーストラリア産オパールには3〜5％の水が含まれています。一般的に、鉱山労働者が掘るほど、オパールの含水量は多くなります。ライティングリッジの鉱山は約30メートルまで下がり、鉱山労働者はオパールの安定度を測定できます。ポーチがタフなドライマテリアルから湿ったウェットポーチに変化するとき、それは安定したマテリアルの指標です。彼らが深く行くと、鉱山労働者はこのオパールが明らかにより多くの水分を含むことを知っています。

ほとんどのオーストラリア産オパールは非多孔性なので、水を吸収しません。

ポーチライン

一部のオパールは、静脈またはクモの巣の線を示す場合があります。これらは亀裂ではなく、ポッチラインです。クラックラインは光を反射しますが、ポッチラインは反射しないので、カッターは簡単にチェックできます。ポッチラインはラインの重症度に応じてオパールの価値を減らします。それらは一般にオパールの安定性に影響を与えません。

エチオピアのオパール

エチオピアのオパールは、ハイドロファンオパールです。ハイドロファンオパールは水を吸収します。エチオピアのオパールが脱水されると、ベースはより不透明になります。オパールが水和すると、より透明になります。水和状態から脱水状態への移行時間は数分から数日までさまざまですが、ほとんどのオパールは数時間で移行します。

破壊試験エチオピアのオパール

原石は、何世紀にもわたって破砕されたり、切断されたりして、荒い素材の分離や切断をテストしてきました。すべての主要な彫刻または切削センターは、切削または彫刻の前に試験材料を破壊します。

現代の試験技術が発明される前でさえ、荒い材料はまだ試験されました。冬の間、薪の火が部屋を暖め、冷たい水が荒地に繰り返し飛び散った。

今日、この基本的なプロセスは、オパールを水に浸し、暖かい環境ではなく高温の環境で乾燥させることにより、オパールに使用されています。このプロセスは、切断プロセスが始まる前に数回繰り返すことができます。小さな亀裂線のあるオパールは、水の下で膨張することがあります。

このプロセスは応力点をテストし、亀裂は最も弱い劈開点に現れます。これでオパールは、目に見える亀裂を取り除くための切断と研磨の準備ができました。

骨折またはひび割れおよび亀裂は次のように表示されます。

粒状の甘いパターン
スムーズな休憩
荒削りで不規則な切れ目

カッターは明らかに、オパールのどちら側にフラクチャーが発生するかを観察するために、オパールがフラクチャーテストされた後にカットすることを決定します。これには優れたスキルが必要であり、骨折が完了したときに開いた方向に従ってプロのカッターが切断します。

オパールを切るための最良のアプローチを理解するには、長年の経験が必要です。マスターオパールカッターは、トップストーンに対して3〜5％のパーセンテージカット料金を請求します。ほとんどの場合、これは支払う価値があります。

オプティコンの安定化

Opticonはオパールを安定させるための最も一般的な形態です。石を覆うのに十分なOpticonで満たされた缶詰スタイルの瓶に石を浸し、水が漏れないように蓋を締めます。結露により樹脂が曇る可能性があります。

瓶が浮かないように十分な水で満たされた通常のスロークッカーに瓶を置きます。
摂氏150〜170度（華氏302〜338度）まで熱を上げます
温度計を使用して温度を確認します。キッチン肉温度計の使用をお勧めします。
24時間調理する
余分な樹脂を濾して、アルミ箔の上に置きます

食品バッグを掃除機で掃除するのと同じような掃除機を使用してください。これは袋から空気を吸います。

少なくとも1時間真空にしてください。
アーティストスタイルのブラシを使用して、樹脂と硬化剤の弱い混合液[40から1]で石をペイントし、15分間再度真空にします。
アセトンクロスで余分な水分を取り除きます。
石が粘着性のある磨きや再磨きではなくなったとき

この54.7カラットのハーレクインパターンのオパールは、1,100ドル以上で販売されていました。 5年前に切り取られたとき、ひび割れた線が表示されました。所有者は石をオプティコンで処理し、未処理の場合はその価値の約10％で販売しました。

接着剤

石を超接着剤でコーティングし、強い光の下で加熱することもできます。石の上を覆うようなガラスは、研磨中の安定性を与えます。

ボルダーオパール

ボルダーオパールは、ほとんどがアイアンストーンのバッキングで形成され、安定しています。このアイアンストーンは、濃い茶色のチョコレート色から薄茶色の砂質のアイアンストーンになります。 Ironstoneは、オパールを安定させるのに役立ちます。いくつかの亀裂線が45％の角度の天使に表示される場合がありますが、オパールはまだ安定しています。一部のボルダークリスタルオパールにも亀裂が見られる場合があります。 KoroitとYowahのオパールフィールドは安定していると見なされます。

メキシコオパール

ほとんどのメキシコ産オパールは安定しています。ポーチとオパールの圧力しきい値が異なるため、ポーチとオパールが1つにカットされると、オパールがひび割れたりひび割れたりすることがあります。

USA OPALS

USAオパールは一般に安定しているとは見なされておらず、オパールはほとんどトリプレットで作られているか、安定しています。アメリカのオパールは、含水率が14％に達する可能性があるため、熱狂する傾向があります。

ブラジルオパール

これらは一般に、水分含有量がほとんど5％未満であるため、安定していると見なされます。オパールは半透明から白い半透明です。

ホンジュラスオパール

マトリックス上のホンジュラスオパールは安定していると見なされますが、マトリックス上に形成された一部の結晶に亀裂線が表示される場合があります